Product Details:
|
| Product Name: | Cross Laminated Film For Bitumen Waterproof Membranes | Material: | HDPE |
|---|---|---|---|
| Production Process: | Cross Laminated | Performance: | Thermal Dimensional Stability |
| Thickness: | 0.09-0.26 | Width: | 100-1250mm |
| Color: | Black, Grey, Blue, Green, Etc. | Application: | Underlayment, Waterproofing Membrane |
| Printing: | Can Be Customizable | Sample: | Available |
| High Light: | 260um Cross Laminated Film,90um Cross Laminated Film,0.9mm polyethylene shrink film |
||
Cross Laminated Film For Bitumen Waterproof Membranes
Description:
It is multi-layers laminated film with high strength property, made via three layers co-extrusion
film blown process and special stretching technology. The inner crossed structure differs from
traditional films with one layer or many layers, possesses both thermal stability and dimensional
stability, good bidirectional tear resistance & high tensile strength, as well as high elongation
at bi-direction.
The Production Process:
OUR THREE STEP PROCESS FOR MANUFACTURING HIGH STRENGTH, DURABILITY,
AND QUALITY CROSS LAMINATED FILM.
| Why Cross Laminated? |
| 1. Puncture Resistance: less accidental damage |
| 2. Thermal Dimensional Stability: No fish-mouthing or controlled shrinkage |
| 3. Cold temperature resistant down to -30°C/-20°C |
| 4. Cross laminated film allows waterproofing membranes to bridge gaps in sheathing and is resistant to damage from incidental movement and settling of the roof |
| 5. UV Stability for typical job site exposure |
Parameter:
| NO. | Item | Performance | ||
| SDM-30 | SDM-60 | |||
| 1 | Tensile Property | Tensile Strength/Mpa ≥ | 30 | 50 |
| MaxF/(N/50mm) ≥ | 200 | 300 | ||
| Elongation as MaxF/% ≥ | 200 | |||
| Elongation at break/% ≥ | 250 | |||
| 2 | Sample number of no broken tested by free-falling dart method ≥ | 8 | ||
| 3 | Tear Strength(Nail Shank)/N ≥ | 60 | ||
| 4 | Angle Tear Strength/N ≥ | 25 | ||
| 5 | Thermal Stability | 120 ℃,10min, No bulb, No deformation | ||
| 6 | Cryogenic Flexibility ℃ |
-35℃, No fissure, No delamination |
||
| 7 | Thermal Ageing | Appearance | No bulb, No deformation | |
| Subsequent MaxF/% ≥ | 80 | |||
| Elongation at MaxF/% ≥ | 200 | |||
| Elongation at break/% ≥ | 200 | |||
| 8 | Artificial Weathering | Appearance | No bulb, No deformation | |
| Subsequent MaxF/% ≥ | 70 | |||
| Elongation at MaxF/% ≥ | 180 | |||
| Elongation at break/% ≥ | 180 | |||
About US:
Upass, founded in 2008, now as a governing unit of China Building Waterproof Association,
a vice chairman unit of Professional Committee of China Modified Plastic Association,
an enterprise with Triple A credibility in China Plastic Association, not only assists the
development of the relevant industries, but also upholds the conception of sustainable
development by successive technological innovation. Upass so far has acquired over
100 of intellectual property rights.